#trs_autoadd_1227496305601 { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1227496305601 p { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1227496305601 td { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1227496305601 div { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1227496305601 li { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } /**---json-- {"":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"p":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"td":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"div":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"li":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"}} --**/

摘要: 为了加快工程的施工进度，减少坝体温度控制措施，对马槽河水电站拱坝混凝土的原材料和配合比进行了试验研究。采用外掺轻烧mgo和粉煤灰、选用缓凝型外加剂等方法延缓和降低水化热，不仅可以加快施工进度，还可以减少产生裂缝和渗透。室内观测记录和强度试验结果表明，外掺轻烧mgo混凝土配合比设计满足温度控制要求。

 

关 键 词: 马槽河拱坝;外掺轻烧mgo;微膨胀混凝土;配合比试验研究

 

中图分类号: tu528.55 文献标识码: a

 

1 工程概况

 

马槽河水电站大坝为外掺轻烧mgo混凝土双曲拱坝，最大坝高67.5m，坝顶宽4m，坝底宽9.5m，坝顶弧长142m，厚度比为0.18，河床为对称的“v”型河谷，坝体采用四级配常态c20混凝土，填筑方量约5万m3 。

 

普通混凝土的自生体积变形大多为微收缩，近年来随着膨胀水泥混凝土的研究和发展，人