#trs_autoadd_1234836338147 { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1234836338147 p { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1234836338147 td { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1234836338147 div { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1234836338147 li { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } /**---json-- {"":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"p":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"td":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"div":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"li":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"}} --**/

水泥砼是建筑工程中使用最广泛、用量最多的一种混合材料,它具有许多优点，但也存有一些弱点,如均匀性差、离散性大，容易产生裂缝，尤其以裂缝为突出。它是长期困扰着我们工程技术人员的头痛问题。

 

一、水泥砼裂缝的分类　

　

水泥砼裂缝是混凝土的一种常见病和多发病。病情绝大多数发生于施工阶段，其原因复杂多变，为了分析其成因，试作如下大致分类：

 

从裂缝外观可分成微观裂缝和宏观裂缝两大类。

 

微观裂缝是指肉眼看不到的、水泥砼内部固有的一种裂缝，它是不连贯的。宽度一般在0.05mm以下，但是要比肉眼可见的即宏观裂缝多得多。这种水泥砼本身固有的微观裂缝，在荷载不超过设计规定的条件下，一般视为无害。用实体显微镜观察、x射线或超声波探测仪等物理检验手段都可鉴定出这种裂缝。另外一种最直接的方法就是用渗水观察，一定压力的水可以从水泥砼内部的裂缝中渗透出来。

 

宏观裂缝宽度在0.05mm以上，并且认为宽度小于0.2~0.3mm的裂缝是无害的，但这里必须有个前提，即裂缝不再扩展，为最终宽度。

 

宏观裂缝可分为以下几种：

 

⑴收缩裂缝：在施工阶段因水泥水化热及外部气温的作用引起水泥砼收缩而产生的裂缝。多为规则的条状，很少交叉。常发生在结构变截面处，往往与受力钢筋平行。收缩裂缝多发生在大体积水泥砼中，梁、板、柱等小块体构件，特别是预应力构件极少产生收缩裂缝。水泥砼收缩裂缝危害较大，尤其是暴露在大