#trs_autoadd_1224810056656 { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1224810056656 p { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1224810056656 td { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1224810056656 div { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } #trs_autoadd_1224810056656 li { margin-top: 0px; font-size: 12pt; margin-bottom: 0px; line-height: 1.5; font-family: 宋体 } /**---json-- {"":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"p":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"td":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"div":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"},"li":{"line-height":"1.5","font-family":"宋体","font-size":"12pt","margin-top":"0","margin-bottom":"0"}} --**/

摘　要: 对于建于上世纪50～70年代的水利工程，现在都面临着混凝土耐久性差的问题。混凝土的孔隙率高、水泥石中的水化物稳定性差、水化物大量的游离石灰是影响混凝土耐久性的主要因素。水工混凝土耐久性差的问题要从结构设计、混凝土组成材料和配合比设计、混凝土的施工、混凝土的强度等方面解决。

 

关键词: 混凝土；耐久性；措施

 

在水利与建筑工程中，混凝土是用途最广、用量最大的建筑材料之一。目前现有的水利工程混凝土耐久性差是一个普遍问题，当时的社会条件、技术力量、材料设备、经济能力等因素，是造成耐久性差的主要原因。

 

一、水工混凝土耐久性的概述

 

混凝土耐久性是指在设计使用的年限内抵抗外界环境或本身所产生侵蚀作用的能力，它包括混凝土的质量、环境介质的侵蚀作用和安全使用期三个方面。就混凝土本身质量来说，大致有低水灰比、富配合、振捣密实、充分湿养护、无裂缝的水工钢筋混凝土，一般都很耐久；关于环境介质的侵蚀，包括物理、化学、水溶液、大气、气体等介质的侵蚀作用以及混凝土碳化、氯离子侵入引起的钢筋锈蚀、高速水流冲刷和气蚀、固体碰撞磨损等；而安全使用期，根据建筑物的规模，一般要求50～100年。我国水利上经济规范（sd-139-85）规定，钢筋混凝土及混凝土水工建筑物的使用期，大型为80年，小型为50年。

 

混凝土对大型工程来说意义尤其重大，若耐久性不足，将会产生极严重的后果，甚至对未来社会造成极为沉重的负担。据美国一项调查显示，美国的混凝土基础设施工程总价值约为6万亿美元，每年所需维修费或